[1]陈小薇,樊振通,余功新,等.彩色防滑路面材料组成对其路用性能的影响[J].长安大学学报(自然科学版),2020,40(1):116-124.
　CHEN Xiao wei,FAN Zhen-tong,? YU Gong xin,et al.Influence of color antiskid pavement material compositionon its road performance[J].Journal of Chang’an University (Natural Science Edition),2020,40(1):116-124.
点击复制

彩色防滑路面材料组成对其路用性能的影响()
分享到：

长安大学学报（自然科学版）[ISSN:1006-6977/CN:61-1281/TN]

卷:
第40卷
期数:
2020年1期
页码:
116-124
栏目:
道路工程
出版日期:
2020-01-15

文章信息/Info

Title:
Influence of color antiskid pavement material compositionon its road performance
作者:
陈小薇; 樊振通; 余功新; 胡贵华; 吴平
1. 长沙理工大学 土木工程学院，湖南 长沙 410004； 2. 湖南交通职业技术学院，路桥工程学院，湖南 长沙 410132；〖JP〗3. 长安大学 公路学院，陕西 西安 710064； 4.湖南省交通建设质量安全监督管理局，湖南 长沙 410116；5. 内蒙古路桥集团有限责任公司，内蒙古 呼和浩特 010010）
Author(s):
CHEN Xiaowei1; 2;  FAN Zhen-tong; ? YU Gongxin3;  HU Guihua4;  WU Ping5
1. School of Civil Engineering, Changsha University of Science & Technology, Changsha 410004, Hunan, China;2. School of Road and Bridge Engineering, Hunan Communication Polytechnic, Changsha 410132, Hunan, China;〖JP〗3. School of Highway, Changan University, Xian 710064, Shaanxi, China; 4. Hunan TrafficConstruction Quality and Safety Supervision Administration, Changsha 410116, Hunan, China;5. Inner Mongolia Road and Bridge Group Co., Ltd., Hohhot 010010, Inner Mongolia, China）
关键词:
道路工程; 道路材料; 彩色路面; 组成设计; 路用性能; 耐久性
Keywords:
road engineering;  road material;  color pavement;  composition design;  road performance;  durability
文献标志码:
A
摘要:
为确定材料组成对彩色防滑路面材料性能的影响，综合考虑防滑粒料粒径、级配及胶黏剂用量，制备了3种彩色防滑路面材料。通过高温车辙试验、表面构造深度和抗滑摆值试验，对比分析了3种彩色防滑路面材料的高温性能和抗滑性能；利用湿轮磨耗仪、四轮磨耗仪进行了不同条件下的磨耗试验及加速加载试验，系统研究了3种彩色防滑路面材料的耐久性能，进而确定了彩色防滑路面的最佳材料组成。研究结果表明：3种彩色防滑路面材料均具有良好的路用性能，当4.75~2.36 mm集料用量为100%、胶黏剂撒布量为2.5 kg/m2时，彩色防滑路面材料的动稳定度最高，为8 077次/mm，抗滑摆值最大，为82，表明该彩色防滑路面材料的高温、抗滑性能最优；3种彩色防滑路面材料均具有良好的耐久性能，当4.75~2.36 mm集料用量为100%、胶黏剂撒布量为2.5 kg/m2时，彩色防滑路面材料1 h浸水条件下的磨耗值为70 g/m2，高温条件下的磨耗值为64.7 g/m2，紫外老化条件下的磨耗值为105.88 g/m2，10%HCL溶液腐蚀条件下的磨耗值为64.7 g/m2；在加速加载5万次磨耗后，该彩色防滑路面材料磨耗质量损失为43.3 g，磨耗值及质量损失均小于其他材料组成，且满足相关规范要求，表明该种材料组成的彩色防滑路面材料的耐久性能最优。〖
Abstract:
To determine the influence of material composition on the performance of color antiskid pavement materials, three kinds of color antiskid pavement materials with different material compositions were prepared considering the particle size, gradation, and amount of adhesives. Through rutting, surface structure depth, and antiskid pendulum tests, the hightemperature performance and antiskid performance of these pavement materials were compared and analyzed. Furthermore, their durabilities were studied systematically based on wear test under different environmental conditions and an accelerated loading test system, a wet wheel and four wheel abrasion instruments were used. The results show that the three kinds of color antiskid pavement materials have a suitable pavement performance, when the aggregate content of 4.75 to 2.36 mm is 100% and the adhesive spreading amount is 2.5 kg/m2, the dynamic stability and antiskid pendulum value of the color antiskid pavement material are the highest. These values are 8077 times/mm and 82 respectively. Meanwhile, the three kinds of color antiskid pavement materials were demonstrated to have a suitable durability, when the aggregate content of 4.75 to 2.36 mm is 100% and the adhesive spreading amount is 2.5 kg/m2, the wear value of the color antiskid pavement material is 70 g/m2 under the conditions of 1 h soaking, 64.7 g/m2 under a hightemperature condition, 105.88 g/m2 under a ultravioletaging condition, and under the condition of 10% HCL solution corrosion, the wear value is also 64.7 g/m2, after 50 000 wears, the wear mass loss is 43.3 g. The wear value and mass loss are less than those of other material compositions and all meet the normative requirements indicating the optimum durability of the color antiskid pavement material. 5 tabs, 9 figs, 31 refs.

相似文献/References:

[1]武建民,祝伟,马士让,等.应用加权密切值法评价基质沥青抗老化性能[J].长安大学学报(自然科学版),2012,32(01):0.
[2]张宜洛,袁中山.SMA混合料结构参数的影响因素[J].长安大学学报(自然科学版),2012,32(01):0.
[3]陈璟,袁万杰,郝培文,等.微观指标对沥青热稳定性能的影响[J].长安大学学报(自然科学版),2012,32(01):0.
[4]周兴业,刘小滔,王旭东,等.基于轴载谱的沥青路面累计当量轴次换算[J].长安大学学报(自然科学版),2012,32(01):0.
[5]李祖仲,王伯禹,陈拴发,等.轴载对复合式路面应力吸收层荷载应力的影响[J].长安大学学报(自然科学版),2012,32(01):0.
[6]关博文,刘开平,陈拴发,等.水镁石纤维路面混凝土路用性能[J].长安大学学报(自然科学版),2012,32(01):0.
[7]翁效林,王玮,张留俊,等.拓宽路基荷载下管桩复合地基沉降变形模式[J].长安大学学报(自然科学版),2012,32(01):0.
[8]穆柯,王选仓,柳志军,等.基于非饱和渗流原理的路基含水率预估[J].长安大学学报(自然科学版),2012,32(01):0.
[9]李振霞,陈渊召.不同类型半刚性基层材料性能的试验与分析[J].长安大学学报(自然科学版),2012,32(01):0.
[10]马 骉,马 晋,周宇鹏.沥青混合料降温收缩断裂特性[J].长安大学学报(自然科学版),2012,32(03):1.
　MA Biao,MA Jin,ZHOU Yu-peng.Cooling shrinkage fracture characteristic of asphalt mixture[J].Journal of Chang’an University (Natural Science Edition),2012,32(1):1.

更新日期/Last Update: 2020-01-17