[1]王朝辉,舒诚,韩冰,等.高模量沥青混凝土研究进展[J].长安大学学报(自然科学版),2020,40(1):1-15.
 WANG Chao hui,SHU Cheng,HAN Bing,et al.Research progress of high modulus asphalt concrete[J].Journal of Chang’an University (Natural Science Edition),2020,40(1):1-15.
点击复制

高模量沥青混凝土研究进展()
分享到:

长安大学学报(自然科学版)[ISSN:1006-6977/CN:61-1281/TN]

卷:
第40卷
期数:
2020年1期
页码:
1-15
栏目:
道路工程
出版日期:
2020-01-15

文章信息/Info

Title:
Research progress of high modulus asphalt concrete
作者:
王朝辉舒诚韩冰傅一周骊巍
1. 长安大学 公路学院,陕西 西安 710064; 2. 齐鲁交通发展集团有限公司,山东 济南 250101;3. 天津市市政工程设计研究院,天津 300051)
Author(s):
WANG Chaohui SHU Cheng HAN Bing FU Yi ZHOU Liwei
1. School of Highway, Changan University, Xian 710064, Shaanxi, China; 2. Qilu TransportationDevelopment Group Co. Ltd., Jinan 250101, Shandong, China; 3. Tianjin Municipal EngineeringDesign & Research Institute, Tianjin 300051, China
关键词:
道路工程高模量沥青混凝土性能评价力学性能路用性能
Keywords:
road engineering high modulus asphalt concrete performance evaluation mechanical property road performance
文献标志码:
A
摘要:
为进一步提升路面结构与材料的耐久性,促进高模量沥青混凝土(high modulus asphalt concrete,HMAC)的研究与应用,系统梳理了国内外现有研究与应用成果,对比法国、欧洲及中国HMAC相关规范与评价指标,总结分析国内外试件成型方式及技术指标差异;全面调查了国内外HAMC相关研究动态,总结了各国高模量技术体系转换成果,对比评价了中国采用低标号(硬质)沥青、自调和沥青、添加聚烯烃类物质(外掺剂)3种方法制备的HMAC力学性能及路用性能,并针对其低温性能缺点提出了改善建议。结果表明:国内外HMAC相关规范对动态模量均要求大于14 GPa,部分国家引入高模量技术后结合本国实情对技术体系进行了转换,导致不同地区试件成型方法与性能验证试验呈差异化;国外制备的HMAC高温性能多采用动态模量、动稳定度及车辙深度等指标评价,均值分别可达15 836 MPa、7 393 次/mm、2.34 mm;中国则主要考虑动态模量与动稳定度等指标,其中采用低标号沥青时动态模量最高,均值可达20 827 MPa,采用外掺剂时动稳定度、疲劳寿命最优,均值分别可达11 640 次/mm、146 173次(应变400×10-6),使用不同种类外掺剂的混合料路用性能差距明显;HMAC低温抗裂性能普遍较差,可掺入胶粉、聚乙烯等助剂予以提升。鉴于中国低标号沥青发展的局限,合理优选性能稳定的外掺剂并改善混合料低温性能是促进HMAC发展的基础。
Abstract:
To further improve the durability of pavement and road materials, promoting the application of high modulus asphalt concrete (HMAC), existing research and application results in China as well as foreign research were reviewed. The relative standards and evaluation indexes of HMAC in France, Europe and China were compared. The conversion results of high modulus technology and technical indexes were clarified. With the comparison of mechanical properties and pavement performance of HMAC prepared by lowgrade hard asphalts, blended asphalts, and polyolefins (admixtures), suggestions were put forward to improve its lowtemperature performance. The results show that the relevant standards of HMAC in various countries stipulate that the dynamic modulus should be greater than 14 GPa. However, the transformation of HMAC in different countries distinguishes between the forming methods and performance verification tests of specimens. Dynamic modulus, stability, and rutting depth are often used to evaluate the hightemperature performance of HMAC prepared abroad, of which the average values are 15 836 MPa, 7 393 times/mm and 2.34 mm, respectively. In China, dynamic modulus and dynamic stability are the main hightemperature performance indicators. Among these three methods, the dynamic modulus of lowgrade hard asphalt HMAC is the highest, with a mean value of 20 827 MPa, but the dynamic stabilities and fatigue properties of admixture HMAC are the best, with a mean value of 11 640 times/mm and 146 173 times (400×10-6 strain levels). The differences between the road performance of mixtures with different admixtures is evident. Most HMACs have poor crack resistance at low temperatures, which could be improved by adding rubber powder, PE, etc. Considering the development limitations of lowgrade hard asphalts in China, it is necessary to find suitable additives and improve the lowtemperature performances of mixtures to promote the development of HMAC. 1 tab, 9 figs, 66 refs.

相似文献/References:

[1]武建民,祝伟,马士让,等.应用加权密切值法评价基质沥青抗老化性能[J].长安大学学报(自然科学版),2012,32(01):0.
[2]张宜洛,袁中山.SMA混合料结构参数的影响因素[J].长安大学学报(自然科学版),2012,32(01):0.
[3]陈璟,袁万杰,郝培文,等.微观指标对沥青热稳定性能的影响[J].长安大学学报(自然科学版),2012,32(01):0.
[4]周兴业,刘小滔,王旭东,等.基于轴载谱的沥青路面累计当量轴次换算[J].长安大学学报(自然科学版),2012,32(01):0.
[5]李祖仲,王伯禹,陈拴发,等.轴载对复合式路面应力吸收层荷载应力的影响[J].长安大学学报(自然科学版),2012,32(01):0.
[6]关博文,刘开平,陈拴发,等.水镁石纤维路面混凝土路用性能[J].长安大学学报(自然科学版),2012,32(01):0.
[7]翁效林,王玮,张留俊,等.拓宽路基荷载下管桩复合地基沉降变形模式[J].长安大学学报(自然科学版),2012,32(01):0.
[8]穆柯,王选仓,柳志军,等.基于非饱和渗流原理的路基含水率预估[J].长安大学学报(自然科学版),2012,32(01):0.
[9]李振霞,陈渊召.不同类型半刚性基层材料性能的试验与分析[J].长安大学学报(自然科学版),2012,32(01):0.
[10]马 骉,马 晋,周宇鹏.沥青混合料降温收缩断裂特性[J].长安大学学报(自然科学版),2012,32(03):1.
 MA Biao,MA Jin,ZHOU Yu-peng.Cooling shrinkage fracture characteristic of asphalt mixture[J].Journal of Chang’an University (Natural Science Edition),2012,32(1):1.
[11]沙爱民,周庆华,杨琴.高模量沥青混凝土材料组成设计方法[J].长安大学学报(自然科学版),2009,29(03):1.
 SHA Ai-min,ZHOU Qing-hua,YANG Qin.Material composition design method for high modulus asphalt concrete[J].Journal of Chang’an University (Natural Science Edition),2009,29(1):1.
[12]周庆华,沙爱民. 高模量沥青混凝土路面永久变形[J].长安大学学报(自然科学版),2013,33(05):13.

更新日期/Last Update: 2020-01-17